To meet the diverse requirements of our clients, we supply exclusive range of AF Oil 220 Non Asbestos Jointing Gasket Sheets. Owing to our in-depth industry experience and precise knowledge of this domain, we are able to manufacture an outstanding assortment of this product. AF Oil 220 Non Asbestos Jointing Gasket Sheets are highly acknowledged in the market due to its durability, optimum strength and ruggedness.
Properties | Testing Method | Unit | Specification |
Density | ASTM F 1315 | G/cm3 | 1.6-1.9 |
Compressibility | ASTM F 36J | % | 7-17 |
Recovery | ASTM F 36 J | % | 40 |
Tensile Strength (Across Grain) | ASTM F 152 | N/mm2 | 9 |
Creep Relaxation (0.80mm) | ASTM F 38 B | % | 35 |
Stress Relaxation | DIN 52913 | | |
a. 16 hours, 175°C | 50 Mpa | Mpa | 20 |
b. 16 hours, 300°C | 50 Mpa | Mpa | |
Gas Solubility (0.80 mm) | ASTM F 37 B | M/hour | 1.0 |
Cold/Hot Compression (0.80 mm) | | | |
a. Thickness decrease at 23°C | | % | |
b. Thickness decrease at 300°C | | | |
ASTM OIL NO 3 (5 HRS, 150°C) | | | |
Thickness Increase | | % | 15 |
Weight Increase | | % | 15 |
10. Fuel B (5 hrs, 23°C) | | | |
Thickness Increase | | % | 15 |
Weight Increase | | % | 15 |
11. Water (5 hrs, 100°C) | | | |
Thickness Increase | | % | 10 |
Weight Increase | | % | 15 |
12. Thickness Increase | | | |
65% H2S04 Acid (48 hrs, 23°C) | | % | |
96% H2S04 Acid (48 hrs, 23°C) | | % | |
40% HNO3 Acid (48 hrs, 23°C) | | % | |
ASTM Line call out | | | ASTM 104 F712122E23A9B9M9 |
Max. Operating Conditions | | | |
Max. Peak Temperature | | ºC | 300 |
Max. Operating Temperature | | ºC | 220 |
Max. Operating Pressure | | Bar | 80 |
![]() |