With the aid of knowledgeable workers, we are engaged in supplying comprehensive range of AF GP Steel 200 Non Asbestos Jointing Gasket Sheets. These sheets are properly tested by our quality inspectors on various parameters to ensure their quality and flawlessness. AF GP Steel 200 Non Asbestos Jointing Gasket Sheets are widely used in engineering and automobile industries.
Properties | Testing Method | Unit | Specification |
Density | ASTM F 1315 | G/cm3 | 1.7-2.0 |
Compressibility | ASTM F 36J | % | 7-17 |
Recovery | ASTM F 36 J | % | 40 |
Tensile Strength (Across Grain) | ASTM F 152 | N/mm2 | 8 |
Creep Relaxation (0.80 mm) | ASTM F 38 B | % | 40 |
Stress Relaxation | DIN 52913 | | |
a. 16 hours, 175°C | 50 Mpa | Mpa | 17 |
b. 16 hours, 300°C | 50 Mpa | Mpa | |
Gas Solubility (0.80 mm) | ASTM F 37 B | M/hour | 1.0 |
Cold/Hot Compression (0.80 mm) | | | |
a. Thickness decrease at 23°C | | % | |
b. Thickness decrease at 300°C | | | |
ASTM OIL NO 3 (5 HRS, 150°C) | | | |
Thickness Increase | | | 15 |
Weight Increase | | | 20 |
10. Fuel B (5 hrs, 23°C) | | | |
Thickness Increase | | % | 20 |
Weight Increase | | % | 20 |
11. Water (5 hrs, 100°C) | | | |
Thickness Increase | | % | 10 |
Weight Increase | | % | 15 |
12. Thickness Increase | | | |
65% H2S04 Acid (48 hrs, 23°C) | | % | |
96% H2S04 Acid (48 hrs, 23°C) | | % | |
40% HNO3 Acid (48 hrs, 23°C) | | % | |
ASTM Line call out | | | ASTM 104 F712232E344966M4 |
Max. Operating Conditions | | | |
Max. Peak Temperature | | ºC | 250 |
Max. Operating Temperature | | ºC | 200 |
Max. Operating Pressure | | Bar | 80 |
![]() |